||The texture and rotation movements of Ag nano particles and nano films|
|Date of Defense
||Thermal evaporator was used to coat a layer of silver nano-particles and thin film on (100) plane of rock salt .|
The experiment content can be divide into three parts .
In the first part , the (100) texture of Ag nano-film and the evolution of the microstructure during annealing were studied . Little change in microstructure was found during low temperature annealing . In the second part , the salt surface was treated with deionized water and chlorine to try to align the Ag nano-particles on its surface . The effect of annealing on the texture and the defects of the Ag nano-particles were analyzed . The stacking fault was found to form early in the nucleation stage . In the third part , Ag nano-particles were scattered on the (100) texture , Ag nano-film and their rotation was studied by annealing at different temperature . Most Ag nano-particles were confirmed to rotate to a parallel orientation relationship with the Ag nano-film .
||Shen, Pouyan - chair|
Kao Po-We - co-chair
Gan, Der shin - advisor
indicate in-campus access in a year and off_campus not accessible|
|Date of Submission